Study of Microstructure and Mechanical Properties of Transient Liquid Phase bonded of Al / Al2O3

مهندسی متالورژی و مواد

Article 6, Volume 28, Issue 2 - Serial Number 16, August 2017, Pages 113-123   

Document Type: Original Articles

DOI: 10.22067/ma.v28i2.36654

Authors

mona yarahmadi^* ; morteza shamanian; hamidreza salimi jazi

Isfahan University Technology

Abstract

Todays, aluminum matrix composites are widely used in many industrial applications due to their superior properties such as high strength to weight ratio. However, joining problems of these composite materials is a challenge which limits their applications. Consternation of alumina particles, micro-cracks and porosity were found in the joint areas that were filled from α-Al solid phase and fine CuAl2 precipitated particles. The filled areas increased as the joint temperature increase. It is due to a higher amount of the molten material produced during joining. Moreover, the amount of CuAl2 precipitated particles reduced as the joining temperature increased, resulting in reduction of the hardness of the α-Al solid phase in the joint area. The shear strength of the bonded joints was also evaluated using a tension test system. The maximum shear strength (82% of the base metal shear strength) was achieved at the bonding temperature of 590°C and process duration of 30 minutes. Analysis of the fractured surfaces showed plastic deformation, shear dimples and partially ductile failure. Some alumina particles were observed on the fractured surface. At low joining temperatures, the joint strength improved by increasing bonding time, whiles at high joining temperatures, the joint strength decreased due to reduction of CuAl2 particles in the α-Al solid phase.

Keywords

Aluminum Matrix Composite; Transient Liquid Phase; Interlayer; Alumina Particles; Isothermal Solidification

Supplementary Files

9-yarahmadi_AK_EDITS.pdf

References

1. Zhang G., Zhang J., Pei Y., Li S., Chai D., “Joining of Al2O3p/Al Composites by Transient Liquid Phase (TLP) Bonding and a Novel Process of Active-Transient Liquid Phase (A-TLP) bonding", Materials Science and Engineering, Vol. 488, pp. 146–156, (2010).

2. Yan J., Xu Z., "Interface Structure and Mechanical Performance of TLP bonded Joints of Al2O3p/6061Al Composites using Cu/Ni Composite Interlayers", Scripta Materialia, Vol. 51, pp. 147-150, (2004).

4. MacDonald W.D., Eagar T.W., “Transient Liquid Phase Bonding Processes”, The Minerals, Metals and Materials Society, Vol. 321, pp. 93–101, (1992).

5. Grant O., Cook C.D., “Overview of Transient Liquid Phase and Partial Transient Liquid Phase bonding”, Sorensen Springer Science, Vol. 245, pp. 25–34, (2011).

6. Nakagawa H., Lee C.H., North T.H., "Modelling of Base Metal Dissolution Behavior During Transient Liquid Phase Brazing", Metallurgical Transactions, Vol. 22A, pp. 543-555, (1991).

7. Tuah-Poku I., Dollar M., Massalski T.B., "A Study of the Transient Liquid Phase Bonding Process Applied to a Ag/Cu/Ag Sandwich Joint", Metallurgical Transactions, Vol. 19A, pp. 675-686, (1988).

8. AlHazaa A., Khan T.I., Haq I., "Transient Liquid Phase (TLP) Bonding of Al7075 to Ti–6Al–4V alloy", Materials Characterization, Vol. 61, pp. 312-317, (2010).

9. Kuntz M.L., “Quantifying Isothermal Solidification Kinetics During Transient Liquid Phase Bonding using Differential Scanning Calorimetry”, Materials and Design, Vol. 44, pp. 1-12, (2006).

10. Dinkel M.K., Heinz P., Pyczak F., Volek A., Ott M., Affeldt E., Vossberg A., Goken M., “Proceedings of the International Symposium on Superalloys”, Materials Science and Engineering, Vol. 211, pp. 23-35, (2008).

11. Abdelfattah M., “An experimental and theoretical study of transient liquid phase bonding of nickel based materials”. Materials and Design, Vol. 39, pp. 893-899, (2008).

12. Kavian O., Cooke Tahir I., Khan Gossettd O., “Nanostructure Particle-Reinforced Transient Liquid Phase Diffusion Bonding”, A Comparative Study The Minerals, Metals & Materials Society and ASM International, Vol. 6, pp. 79-91, (2011).

13. Wikstrom N.P., “The Effect of Process Parameters on Microstructure of Transient Liquid Phase Bonded Super Alloys Inconel 738 and Waspaloy”, Materials Science and Engineering, Vol. 35, pp. 456-467, (2006).

14. Lugscheider E., Ferrara S., Janssen H., Reimann A., Wildpanner B., “Progress and Developments in the Field of Materials for Transient Liquid Phase Bonding and Active Soldering Processes”, Materials Science and Engineering, Vol. 30, pp. 87-94, (2006).

15. Zhang G., Zhang J., Pei Y., Li S., Chai D., “Joining of Al2O3p/Al Composites by Transient Liquid Phase (TLP) Bonding and a Novel Process of Active-Transient Liquid Phase (A-TLP) Bonding”, Materials Science and Engineering, Vol. 488, pp. 146–156, (2008).