Microstructure and Mechanical Properties of a Low Alloy High Carbon Steel Processed by Quenching and Partitioning Process

مهندسی متالورژی و مواد

Article 6, Volume 26, Issue 1 - Serial Number 11, March 2015, Pages 105-116   

Document Type: Original Articles

DOI: 10.22067/ma.v26i1.27922

Authors

Abdollah Shirali^* ; Abbas Honarbakhsh Raouf; Soheila Bazzaz Bonabi

Semnan University

Abstract

The quenching and partitioning (Q&P) process is a new heat treatment cycle to produce the third generation of advanced high strength steels based on diffusion of carbon from martensite to retained austenite phase. The application of this process for various steels leads to a remarkable combination of mechanical properties including high strength and good ductility. Using this process in automotive industry causes better mechanical performance, greater car safety, weight saving and cost reduction. In this study, a low alloy high carbon steel has been subjected to Q&P process and its microstructure and mechanical properties have been investigated. The results showed that the microstructure of the quenched and partitioned steel contains carbon-enriched stabilized austenite and carbon-depleted martensite resulting in increasing the strength of steel with an acceptable ductility. Conducting Q&P heat treatment caused the retained austenite content and the hardness of steel to increase. Fracture in specimens treated by Q&P process was of brittle type and their fracture surface was considered to be quasi-cleavage.

Keywords

quenching; Partitioning; retained austenite; martensite

References

Speer, J.G., De Moor, E., Findley, K.O., Matlock, D.K., De Cooman, B.C. and Edmonds, D.V.,“Analysis of Microstructure Evolution in Quenching and Partitioning Automotive Sheet Steel”, Metallurgical and Materials Transactions A, Vol. 42A, pp. 3591-3601, (2011).

2. Matlock, D.K., Speer, J.G., De Moor,E. and Gibbs, P.J., “Recent Developments in Advanced High Strength Sheet Steels for Automotive Applications: An Overview”, JESTECH, Vol. 15(1), pp. 1-12, (2012).

3. Qu, H., “Advanced High Strength Steel through Paraequilibrium Carbon Partitioning and Austenite Stabilization”, Master’s Thesis, Department of Materials Science and Engineering, Case Western Reserve University, (2011).

4. Jirkova, H., Kučerova,L. and Mašek, B., “Effect of Quenching and Partitioning Temperatures in the Q-P Process on the Properties of AHSS with Various Amounts of Manganese and Silicon”, Materials Science Forum, Vols. 706-709, pp. 2734-2739, (2012).

5. Edmonds, D.V., He, K., Rizzo, F.C., De Cooman, B.C., Matlock,D.K. and Speer, J.G., “Quenching and partitioning martensite—A novel steel heat treatment”, Materials Science and Engineering A, Vols. 438-440, pp. 25-34, (2006).

6. Santofimia, M.J., Zhao, L., Petrov, R., Kwakernaak, C., Sloof, W.G. and Sietsma, J., “Microstructural development during the quenching and partitioning process in a newly designed low-carbon steel”, Acta Materialia, Vol. 59, pp. 6059-6068, (2011).

7. Speer, J.G.,Edmonds, D.V.,Rizzo,F.C. and Matlock, D.K.,“Partitioning of carbon from supersaturated plates of ferrite, with application to steel processing and fundamentals of the bainite transformation”, Current Opinion in Solid-State and Materials Science, Vol. 8, pp. 219-237, (2004).

8. Santofimia, M.J.,Nguyen-Minh, T., Zhao, L.,Petrov, R.,Sabirov,I. and Sietsma, J.,“New low carbon Q&P steels containing film-like intercritical ferrite”, Materials Science and Engineering A, Vol. 527, pp. 6429-6439, (2010).

9. Santofimia, M.J.,Zhao, L.,Petrov,R. and Sietsma, J.,“Characterization of the microstructure obtained by the quenching and partitioning process in a low-carbon steel”, Materials Characterization, Vol. 59, pp. 1758-1764, (2008).

10. Santofimia,M.J.,Zhao,L.and Sietsma,J.,“Overview of Mechanisms Involved During the Quenching and Partitioning Process in Steels”, Metallurgical and Materials Transactions A, Vol. 42A, pp. 3620-3626, (2011).

11. Sun,J. and Yu,H.,“Microstructure development and mechanical properties of quenching and partitioning (Q&P) steel and an incorporation of hotdipping galvanization during Q&P process”, Materials Science and Engineering A, Vol. 586, pp. 100-107, (2013).

12. Liu,H.,Jin,X.,Dong,H.and Shi, J.,“Martensitic microstructural transformations from the hot stamping, quenching and partitioning process”, Materials Characterization, Vol. 62, pp. 223-227, (2011).

13. Nayak, S.S.,Anumolu, R.,Misra, R.D.K.,Kim,K.H. and Lee, D.L.,“Microstructure–hardness relationship in quenched and partitioned medium-carbon and high-carbon steels containing silicon”, Materials Science and Engineering A, pp. 442-456, (2008).

14. Pastore, E.,De Negri, S.,Fabbreschi, M.,Ienco, M.G.,Pinasco, M.R.,Saccone,A. and Valentini, R.,“Experimental investigation on low-carbon quenched and partitioned steel”, La Metallurgia Italiana, Vol. 9, pp. 25-35, (2011).

15. Kucerova, L.,Aisman, D.,Jirkova, H.,Masek,B.and Hauserova, D.,“Optimization of Q-P process parameters with regard to final microstructures and properties”, Proceedings of the 20th International DAAAM Symposium Intelligent Manufacturing & Automation: Theory, Practice & Education, Vol. 20, No. 1, pp. 1035-1036, (2009).

[16. S.C. Hong, J.C. Ahn, S.Y. Nam, S.J. Kim, H.C. Yang, J.G. Speer and D.K. Matlock, “Mechanical Properties of High-Si Plate Steel Produced by the Quenching and Partitioning Process”, Metals and Materials International, Vol. 13, No. 6, pp. 439-445, 2007.

17. Jatczak, C.F.,Larson,J.A. and Shin, S.W.,“Retained Austenite and Its Measurement by X-Ray Diffraction”, Manual SP-452, SAE, (1979).

18. ASTM Standards, “Standard Practice for X-Ray Determination of Retained Austenite in Steel with Near Random Crystallographic Orientation”, E 975 – 03.

19. Cullity, B.D., “Elements of X-ray Diffraction” Addison-Wesley Publishing Company, Inc., Reading, Massachusetts, (1956).

20. ASTM Standards, “Standard Test Methods for Tension Testing of Metallic Materials”, E8/E8M–09.