Fabrication and Study of Wear Properties of AA8090 Composite Reinforced with SiC Particles after Precipitation Hardening with Directional Quenching

مهندسی متالورژی و مواد

Article 7, Volume 28, Issue 1 - Serial Number 15, March 2017, Pages 87-98   

Document Type: Original Articles

DOI: 10.22067/ma.v28i1.34881

Authors

Amir Kebriyaei^* ; Hassan Saghafian; Shamseddin Mirdamadi

School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, Iran

Abstract

AA8090 is an extra light and deformable group of lithium containing aluminum alloys which have recently replaced some aerospace aluminum alloys, such as 2000 and 7000 series, due to their higher elastic modulus and lower specific weight. In this study, AA8090 matrix composites containing 3, 6 and 9 vol.% SiC were cast using a modified stir casting method. The casting billets were deformed though a hot extrusion operation, followed by a precipitation hardening treatment (T6) with directional quenching and aging at 190 °C. Wear tests were conducted before and after the precipitation hardening (at the peak hardness aging time) using the pin-on-disc method at loads of 10, 20 and 30 N. All samples exhibited a mild wear at 10 and 20 N wear loads, which turned into a sever wear at 30 N. It was shown that increasing the SiC content in the composite samples reduces the wear rate. Also, the wear results after precipitation hardening indicated a decrease in the wear rate only at the wear loads of 10 and 20 N. At the wear load of 30 N, the wear rate increased after precipitation hardening. This behavior was attributed to a transition in the wear mechanism from abrasive to adhesive by increasing the load.

Keywords

AA8090; Composite; Age Hardening; directional Quenching; wear

References

1. Cho A., "Low Density High Strength Al-Li Alloy", Patent number: 5,198,045, (1993).

2. Yurko J.A., "Advanced in Lightweight Automotive Casting", SAE International, pp. 19, (2003).

3. James R.S., "Aluminum-Lithium Alloys". Metals Handbook, 10th Edition, Vol. 2, pp. 178-199, (1994).

4. Razavi S.H., Mirdamadi Sh., Arabi H., Szpunar J., “Mathematical Model of Influence of Rapid Induction Heating on Nucleation and Growth of Precipitates”, Material Science and Technology, Vol. 17, pp.1205-1210, (2001).

5. نوری حسین آبادی س.، میردامادی ش.، هادوی م.م.، " بهبود داکتلیته ورق آلیاژ 8090 Al از طریق عملیات حرارتی کوئنچ جهت دار در سطح آزمایشگاهی"، کمیسیون عالی ثبت اختراعات، اکتشافات و نوآوریهای صنایع دفاعی و مراکز تحقیقاتی وابسته به نیروهای مسلح، 900000234 ب، )1389(.

6. کبریائی ا.، میردامادی ش.، ثقفیان ح.، "بررسی اثر عملیات حرارتی بر خواض نریبولوژیکی و مکانیکی کامپوزیت AA8090/6%SiCp"، مجلۀ علمی پژوهشی فرایندهای نوین در مهندسی مواد، دوره 8، شماره 4، )1393(.

7. Dong S.L., Mao J.F., Yang D.Z., Cui Y.X., Jiang L.T., “Age-hardening behavior of a SiCw/Al-Li-Cu-Mg-Zr composite”, Materials Science and Engineering A, Vol. 327, pp. 213-223, (2002).

8. Lee H.F., Boey F., Khor K.A., Sano T., “High deformation consolidation CIP:hot extrusion process for a 8091 Al–Li:SiC composite”, Mater. Sci. Eng. A, Vol. 189, pp. 173–180, (1994).

9. Ghomashchi M.R., Vikhrov A., “Squeeze casting: an overview”, Journal of Materials Processing Technology, Vol. 101, pp. 1-9, (2000).

10. Burakowfkio T. , WierzchonT., “Surface engineering of Metals, Principle, Equipment, Technologies”, CRC Press LLC, (1999).

11. Bhushan B., “Introduction to Tribology”, John Wiley & Sonse, INC., (2002).

12. Hutching I.M., “Tribology and Wear of Engineering Materials”, (1992).

13. Bauri R., Surapa M.K., “Sliding wear behavior of Al-Li-SiCp composites”, Wear, Vol. 265, pp. 1756-1766, (2008).

14. Gokhale A.A., Singh V., "Effect of Zr Content and Mechanical working on the structure and tensile properties of A.A.8090 Alloy Plates", Journal of Materials Processing Technology, Vol. 159, pp. 369-376, (2005).

15. Bauri R., Surappa M.K., “Processing and properties of Al–Li–SiCp composites”, Science and Technology of Advanced Materials, Vol. 8, pp. 494-502, (2007).

16. Nemati N., Khosroshahi R., Emamy M., Zolriasatein A., “Investigation of microstructure, hardness and wear properties of Al–4.5 wt.% Cu–TiC nanocomposites produced by mechanical milling”, Materials and Design, Vol. 32, pp. 3718-3729, (2011).